VẬT LIỆU CHỊU LỬA CƠ BẢN CHO LÒ THỦY TINH

Giá: Liên hệ

Model: VẬT LIỆU CHỊU LỬA CƠ BẢN CHO LÒ THỦY TINH

Nhà sản xuất: LMM

Xuất xứ: China

Danh mục: Gạch chịu nhiệt

HỖ TRỢ KHÁCH HÀNG

74 Trịnh Đình Thảo, Phường Phú Trung, Quận Tân Phú, Thành phố Hồ Chí Minh, Việt Nam
0909 057 026
(028) 3853 6931
Info@pumptech.vn

THỐNG SỐ KĨ THUẬT

Basic refractories for glass furnace.
Our productions have excellent resistance to alkali vapor attack, resistance to change of structureand fine resistance to peeling. They are the good materials for used in regenerator of the glassfurrnace, and widely used in float sheet glass furnace, bottle and other glass production furnace .

		Unit	Fused MgO Brick				MgO-Al2O3 Beick
		Unit	YDMZ-98	YDMZ-97	YDMZ-95	YDMZ-93	YML-80A
Apparent Porosity		%	16.5	16.5	17.0	17.0	18.0
Bulk Density		g/cm3	3.00	3.00	2.95	2.92	2.85
Cold Crushing Strength		MPa	60	60	60	60	40
Refractoriness Under Load T2		℃	1700	1700	1650	1580	1560
Chemical Composition	MgO	%	97.5	97	95	93	80
	Al2O3						9
	SiO2		1.0	1.0	2.5	–

		Unit	Direct-bonded MgO-Cr2O3 Brick			MgO-Cr2O3 Brick
		Unit	YDMC-12	YDMC-10	YU34	YMGe-10	YMGe-8
Apparent Porosity		%	17.5	17.5	18.0	19.0	19.0
Bulk Density		g/cm3	3.02	3.00	3.00	2.96	2.95
Cold Crushing Strength		MPa	45	45	40	40	40
Refractoriness Under Load T2		℃	1700	1700	1680	1580	1580
Chemical Composition	MgO	%	70	75	75	70	72
Chemical Composition	Cr2O3	%	12	10	10	10	8